The Thickness and Opacity of Aesthetic Materials Influence the Restoration of Discolored Teeth.

Abstract

This study aimed to evaluate the influence of thickness and opacity on the ability of composite resin and ceramic veneer restorations to mask discolored teeth. Ninety veneers were made of lithium disilicate ceramic, shades BL1 and 0 (IPS e.max Press, Ivoclar Vivadent), and 60 were made of composite resin, shade BL-L (IPS Empress Direct, Ivoclar Vivadent). The veneers measured 4 mm in width x 4 mm in length and had a thickness of 0.7, 1.0, or 1.2 mm. One hundred and fifty human premolars were selected to obtain 150 dental fragments with the following dimensions: 4 mm x 4 mm x 3 mm (width x length x thickness). The fragments were discolored, submitted to color measurement and randomly assigned to 15 groups (n=10) according to the type and opacity of the restorative material (IPS e.max Press: high translucency [HT], low translucency [LT], and medium opacity [MO]; IPS Empress Direct: dentin and enamel) and thickness of the veneers (0.7, 1.0, and 1.2 mm). After cementation of the ceramic or composite resin veneers using a translucent resin cement (RelyX veneer, 3M), a final color measurement was taken from each specimen and the total color variation (ΔE) was calculated by subtracting the initial and the final color measurement. The final lightness (L*) of the restored dental fragments was also calculated. The highest ΔE values were observed for the LT and MO ceramic groups, followed by dentin composite resin. Regarding the different thicknesses of ceramic veneers, every 1.2-mm-thick group had higher values of ΔE, considering their respective opacities (p<0.05). The highest lightness values were found for the LT and MO ceramic veneers (thickness of 1.2 mm). Dentin-shade composite resins showed similar lightness values in all groups. The best thickness/opacity combinations for masking discolored dental substrates were LT and MO ceramic veneers with 1.2-mm thickness. Dentin-shade composite resin veneers with a thickness of 0.7-1.0 mm showed good ability to mask discolored dental substrates.