Abstract
ABSTRACTThe flexural strength and the single edge notch beam fracture toughness of undoped ZrO2 crystals, grown by the skull melting technique, were examined from room temperature to 1400°C. On heating the toughness increased with test temperature to a maximum of 4.0 MPajm at 1225°C then gradually decreased to 2.6 MPa/m. Upon cooling after a 20 minute hold at 1250°C an increase in toughness to 5 MPa/m was observed at 1200°C; upon cooling to lower temperatures Kic gradually diminished. The loaddeflection curves for the flexural strength tests showed marked nonlinearity before failure for samples tested on cooling. The temperature dependence of the apparent yield stress suggests that initial yielding occurs by slip above 1200°C but that from 1200°C to 1050°C the observed yielding is due to stress induced tetragonal to monoclinic transformation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.