The synergistic effect of polytetrafluoroethylene in-situ fibrillation and dibenzoyl sebacate hydrazide on the crystallization and foaming behavior of poly (lactic acid)

Abstract

The fully degradable poly (lactic acid) foam with green environmental protection characteristics can alleviate the shortage of petroleum resources caused by the application of plastics. However, due to the inherent low melt strength and slow crystallization rate of linear PLA. It is difficult to obtain PLA microcellular foam with good morphology. In order to obtain PLA microcellular foam with ultra-high expansion ratio and small cell size, PTFE (polytetrafluoroethylene) nanofibers with excellent CO2 adsorption rate were introduced. Self-assembled nucleator TMC-300(dibenzoyl sebacate hydrazide) was also introduced to blend with PLA to obtain small-sized cells. The results show that the PTFE entanglement network as a self-assembled template can effectively improve the early crystallization nucleation efficiency and increase the crystallinity of branched PLA (CBPLA)/TMC by 7 %. The microcellular foam with PTFE content of 0.5 wt% (CBPLA/TMC/PTFE 0.5) was successfully prepared by physical foaming agent, which had the lowest cell size (8.7 μm) And high expansion ratio (1200 %).