Abstract
The effect of cold rolling and annealing treatments in two temperatures, 800°C and 900°C on texture formation in duplex steel (X60MnAl30-9) was examined. Texture measurements were carried out using X-ray diffraction and Schulz reflection technique. The mechanical properties i. e. 0.2% proof stress, ultimate tensile strength and elongation were measured for each experimental conditions. It was found that ferrite was characterized by the orientations of a fibre which could be found in cold rolling state and also after the annealing in both temperatures. The weak orientations close to g fibre were observed after the annealing. The cold rolling texture of austenite was a typical texture of cold rolled fcc metals. No significant changes in texture of austenite after the annealing treatments were found.