Abstract
The structure of liquid Fe-C alloy near the melting point has been studied at three different temperatures (1540, 1560 and 1580 °C). It is shown that the structural correlation length (or the cluster size), coordination number, distance between the nearest neighbour atoms and number of atoms in a cluster all decrease with increasing temperature. Small prepeaks before the first main peak were found in the structure factors of liquid alloy and the prepeaks became slightly obscure as the temperature increased. In general, the presence of the prepeaks corresponds to a medium range order structure. The prepeaks fade away with increasing temperature implying that the degree of superheat contributes to the disappearance of the medium range order.On a étudié la structure de l’alliage liquide Fe–C près du point de fusion, à trois températures différentes (1540, 1560 et 1580 °C). On montre que la longueur de corrélation de la structure (ou taille de la grappe), le nombre de coordination, la distance des atomes les plus proches voisins et le nombre d’atomes dans une grappe diminuent tous avec une augmentation de la température. On a trouvé de petits pré–pics avant le premier pic principal dans les facteurs de structure de l’alliage liquide et ceux-ci s’obscurcissaient légèrement à mesure que la température s’élevait. En général, la présence des pré–pics correspond à une structure d’ordre à moyenne portée. Les pré–pics s’estompent avec une augmentation de la température, impliquant que le degré de surchauffe contribue à la disparition de l’ordre à moyenne portée.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have