The structural, optical, and morphological properties of NiO‐Cu prepared by spray pyrolysis technique

Abstract

AbstractThe technique of spray pyrolysis used to prepare the pure thin films NiO and NiO:Cu. In this study, the nickel chloride salt solution (NiCl2⋅6H2O) was used to fabricate thin films deposited on a glass substrate. The structural, optical, and morphological fabricated properties of the samples were investigated. X‐ray diffraction reveals a polycrystalline nickel oxide layer with a crystalline cubic form, with (111), (200), and (222). Atomic force microscopic studied the surface morphology of the thin‐film samples. The fabrication process of growth was at the specific doping ratio (0%, 0.5%, 1%, 1.5%, and 2%) where all thin films had a cubic structure. The energy difference for the NiO and NiO:Cu reference samples have ranged from 3.25 to 3.5 eV. The mobility, magnetoresistance, resistivity, and conductivity were measured and presented as well as the relationship between current‐voltage and current‐resistivity.