In 25% Cr duplex stainless steels, the effect of prior-solution treatment temperature (STT) on the microstructure and corrosion behavior with ageing at 750 °C and 850 °C was investigated. The results revealed that the precipitation rate of σ-phase was fast in the early stage of ageing for 80 min, and then got slower with ageing time up to 330 min. The σ-phase formation was effectively suppressed by raising STT from 1060 °C to 1230 °C especially for ageing at 750 °C. Consequently, the corrosion rate of specimen was dependent on the amount of σ-phase precipitation, and was lowered due to higher STT, and more σ-phase precipitation can lead to the transition from metastable to stable pitting with ageing at 750 °C up to 330 min. Pitting occurred easily around coarse σ precipitates and caused selective dissolution in ferrite. The longer ageing time increased intergranular corrosion (IGC) susceptibility, whereas higher STT contributed to better resistance to IGC.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call