Abstract
ABSTRACT In this research, YSZ-Alumina top coat was deposited on the Hastelloy substrate with a NiCrAlY bond coat by Atmospheric plasma spraying process. YSZ-10 wt-% Al2O3 composite coatings with pyrolysed and un-pyrolysed Al2O3 powder were deposited. High temperature oxidation and thermal shock resistance of both coatings were investigated. Thermal shock test results showed that the lifetime of the YSZ-10 wt-% Al2O3 coating was increased by the pyrolysation of the un-pyrolysed Al2O3. The network of micro-segmented cracks produced by the pyrolysation of the un-pyrolysed Al2O3 improved the strain accommodation, introducing it as the main enhancement mechanism for TBC life extension. Using of pyrolysed alumina, resulted increased in the flattening degree of the splats, and so reduction of porosity and intra-splat cracks. This, in turn, reduced the permeability of the top coat and decreased the rate of oxide growth on the bond coat.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.