Abstract
Experimental work was focused on the restoration of functional surfaces of shaped parts of the molds for high-pressure casting of aluminum alloys. Paper presents results of the research aimed at determination of the quality of renovation layers applied by laser technology and TOP TIG technology. The TruDisk 4002 solid-state disk laser and the AirLiquide TOPTIG 220 welding power source were used to create the layers. Clad was applied to the base material of nickel-chromium-molybdenum vanadium steel 1.2714, DIN-56NiCrMoV7, with a hardness of 44 HRC. Uddeholm Deivar 1.2344, DIN-X40CrMoV51 wire with a 1.2 mm diameter was used as an additive material. The clad quality was evaluated using the light and electron microscopy and EDX microanalysis. The size of the heat affected zone (HAZ) and the presence of internal defects in the clads were determined. HAZ was set as max. a min. Value. Experimental work was supplemented by evaluation of tribological properties of clads by Pin-on-disc method.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.