Abstract
Al doped ZnO (ZnO:Al) thin films were prepared using a sol–gel dip coating technique and deposited on borosilicate glass substrates. The irradiation treatment, was conducted using Co-60 radioisotope, played an important role in enhancing electrical properties. The absorbed dose was a key parameter to decrease the electrical resistivity and to increase carrier density and carrier mobility of nanospherical ZnO:Al thin film. ZnO:Al thin film with the doping of Al at 0.8at% had the lowest electrical resistivity and the highest optical transmittance after the irradiation treatment. Optical properties, such as transmittance and reflectance, were affected at an absorbed dose of 0.2Gy. The curves of optical density were improved at ∼380, 420, and 520nm in visible range after the irradiation process. Besides, another characteristic optical density band between∼900 and 1100nm was enhanced by gamma irradiation. It has been suggested that the mechanism of absorption is related to an allowed direct transition at the irradiated ZnO:Al thin film on borosilicate glass. The optical band gap of the ZnO:Al thin films broadened with increasing doping concentration. However, there is a decrease in optical energy gap of ZnO:Al thin film along with the absorbed dose of the film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.