Abstract
Phosphorus substituted (Pr,Tb)8(Fe,Nb,Zr,P)88B4 nanocomposites have been produced by melt-spinning. The effects of phosphorus substitution as well as wheel speed on the crystallization behavior and magnetic properties of the melt-spun samples have been investigated. With the substitution of phosphorus, the crystallization temperature of amorphous phase increases. The optimum wheel speed was found to be around 25 m/s for as-spun ribbons and 40 m/s for the annealed samples, both of which present excellent second quadrant hysteresis loop shapes due to the fine grain size of α-Fe which is around 20 nm. The addition of phosphorus also greatly improves the coercivity of Pr–Fe–B nanocomposites without a significant loss of saturation magnetization. A higher coercivity of 9.2 kOe in P-substituted samples was obtained as compared to 8.1 kOe in P-free samples. This is attributed to a narrower temperature span between the crystallization into TbCu7 structure and the transformation into the 2:14:1 phase caused by the phosphorus substitution.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.