The Impact of Silver Diamine Fluoride Only or Simultaneously With Potassium Iodide Treatment on the Bond Durability of Resin Composite Material on Primary Teeth.

Abstract

We aim to evaluate the bond strength between resin composite and primary demineralized dentin, pretreated with silver diamine fluoride (SDF) and simultaneous SDF with potassium iodide (KI) after thermal aging. In this in vitrostudy, human carious-free primary molars were randomly assigned into three groups and prepared by exposing the superficial dentin. The primary dentin of each molar was demineralized. The first group (the control) received saline treatment before bond application. SDF was pretreated for the second group, whereas SDF and KI were used for the third. After that, the pretreated dentin was immediately built with resin composite bonded with a universal adhesive and kept wet for 24 hours. Then, the pretreated molars were prepared into beam specimens for microtensile bond strength (µTBS), 16 for each group, and subjected to thermal aging. Lastly, they were tested using a universal testing machine, and the resulting data were analyzed using one-way analysis of variance (ANOVA) followed by Tukey's post hoc test. It was found that the SDF-KI group had a significant difference with both the control and SDF groups (p < 0.05), while the control and SDF groups showed no significant differences (p =0.310). The SDF-KI group had the highest mean value of 11.73 ± 4.39 megapascal (MPa). In contrast, the control group had the lowest mean value of 9.31 ± 3.41 MPa. Post hoc pairwise comparison results showed that SDF-KI pretreatment had a significantly higher strength value than the control and SDF groups. Pretreatment of demineralized primary dentin with SDF-KI does not negatively affect the immediate loading of resin composite. However, under the limitation of this study, KI application after SDF pretreatment is recommended to enhance the bond's durability of resin composite to demineralized dentin.