Abstract
Many buildings along the coast are exposed to the salt spray climate, but the hygric behavior of porous building materials under the influence of salt crystallization are unclear. In this study, an accelerated salt spray test was conducted on cement mortar. For samples with different salt spray cycles, chloride ion content was measured and saturated moisture content (wsat), open porosity (po) and apparent density (ρb) were obtained by a vacuum saturation test, while capillary absorption coefficient (Acap) and capillary moisture content (wcap) were determined from capillary absorption tests using innovative methods. Additionally, the pore characteristics and micromorphology of the samples were examined and analyzed using a mercury intrusion porosimeter (MIP) and a scanning electron microscope (SEM). The results indicate that a large amount of deposited salt crystals mainly clogs pores with a diameter of 0.02 to 0.12 μm, resulting in a 18.7 % decrease in po as well as a 30 % decrease in Acap and a 17.4 % decrease in wcap subjected to 35 salt spray cycles. This finding supports a deeper understanding of fluid moisture absorption and transfer in building envelope materials in coastal areas.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.