The friction behavior of Ni −-, SiO −2- and mica sodium silicate-based solid lubrication composites

Abstract

The friction behavior of Ni −-, SiO − 2- and mica sodium silicate-based lubricant composites, which included BN, WS 2 and graphite as lubricants, were examined. A ring-on-disk apparatus, in which a solid lubricant composite disk was held against a rotating stainless ring, was used as the test configuration. The tests were run with a load from 62 to 250 N in temperatures from 20 to 800°C in the laboratory environment. The wear surface was characterized by scanning electron microscope and X-ray photo spectroscopy. The major findings were that both mica sodium silicate- and SiO − 2-based composites failed at above 500°C due to severe wear and surface damage; in contrast, Ni −-based composite showed a stable friction coefficient and low wear from 20 to 800°C.