Abstract
The effect of Sc and Zr on the fluidity of A357 alloy was investigated using spiral fluidity resin sand molds. The results showed that the order of the fluidity was A357+Zr > A357+Sc > A357 > A357+Zr+Sc. The TDCP and the solidification temperature range were also discussed. With Sc and Zr addition, the TDCP and the solidification temperature range of the alloy were changed, which led to the changes of the fluidity. The order of TDCP was A357+Zr < A357+Sc < A357 < A357+Zr+Sc and the order of the solidification temperature range was A357+Zr < A357+Sc < A357 < A357+Zr +Sc. What’s more, △T2 (△T2=TP-TDCP, TP was pouring temperature) and △T1 (△T1=TN-TDCP, TN was α-Al nucleation temperature) were compared, and △T2 was better suited for fluidity investigation than △T1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.