The feasibility of using solution-processed aqueous La2O3 as effective hole injection layer in organic light-emitting diode

Abstract

Low-cost and scalable manufacturing boosts organic electronic devices with all solution process. La2O3 powders and corresponding aqueous solutions are facilely synthesized. Atomic force microscopy and scanning electron microscopy measurements show that solution-processed La2O3 behaves superior film morphology. X-ray diffraction and X-ray photoelectron spectroscopy measurements verify crystal phase and typical La signals. In comparison with the most widely-used hole injection layers (HILs) of MoOx and poly(ethylene dioxythiophene):poly(styrene sulfonate) (PEDOT:PSS), enhanced luminous efficiency is observed in organic light-emitting diode (OLED) using solution-processed La2O3 HIL. Current-voltage, impedance-voltage and phase angle-voltage transition curves clarify that solution-processed La2O3 behaves nearly comparable hole injection capacity to MoOx and PEDOT:PSS, and favorably tailors carrier balance. Moreover, the hole injection mechanism of solution-processed La2O3 is proven to be predominantly controlled by Fowler-Nordheim tunneling process and the hole injection barrier height between ITO and NPB via La2O3 interlayer is estimated to be 0.098 eV. Our experiments provide a feasible application of La2O3 in organic electronic devices with solution process.