Abstract
The mechanical properties of polyphenylene sulphide (PPS) and liquid crystalline polymer (LCP) blends were investigated over a range of temperatures. The effect of blend composition on the brittle-ductile transition temperature (B-D) was also studied by differential scanning calorimetry and scanning electron microscopy. Blends of various compositions (PPS/LCP; 90/10, 75/25, 50/50 and 25/75) were prepared and injection moulded. The bending test temperature was varied between −40 and 150 °C. The results showed a rapid load drop at the B-D transition region. The B-D transition temperature occurred in unannealed pure PPS, 90/10, 25/75 and 50/50 blends around 75 °C whilst in the annealed sample it was observed around 100 °C. In pure LCP and 25/75, no transition occurred. Partial miscibility of PPS and LCP was confirmed by SEM observations, bending modulus and thermal properties. The use of LCP, as a good reinforcing agent which can improve processability and modulus, is discussed.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call