This study considers the bearing strengths and failure modes of woven-glass–epoxy prepreg composite mechanically fastened joints. For the study, the specimens were immersed in natural seawater in the laboratory for over 1 year. The edge distance-to-hole diameter ( E/ D) ratio and the specimen width-to-hole-diameter ratio ( W/ D) were systematically altered during experiments. Failure modes were determined by observing the failure regions on the specimens. Damage progression in pin-loaded specimens prepared from woven-glass–epoxy prepreg was also examined using a scanning electron microscopy for three different percentages of ultimate failure load. According to the experimental investigation results, it was observed that the bearing load values obtained from the specimens immersed in seawater decreased considerably in comparison to unimmersed specimens.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.