The effects of ferrocene concentration on CNT growth on micron silica gel

Abstract

The growth of CNT on micron size spherical silica gel of high porosity was performed in this work. The CNT was grown via floating catalyst chemical vapor deposition method (FCCVD). The reaction temperature and time were kept at 760 °C and 3 hours, respectively. The concentration of the catalyst used, which was ferrocene, was varied from 1 wt. % to 9.6 wt. %, with respect to toluene. Striking difference in the morphology of the synthesized tubes was observed using Field Emission Scanning Electron Microscope (FESEM) and Transmission Electron Microscope (TEM) images. The quality and quantity of the CNT were further characterized via Raman Spectroscopy and Thermogravimetric Analysis. Based on these characterizations, it was found that the ferrocene concentration greatly affects the morphology of the obtained CNT; with 1 wt.% and 9.6 wt.% ferrocene concentrations yield CNT of bigger outer diameters, compared to the CNT obtained from 5 wt.% ferrocene concentrations.