Abstract
The contributions to fatigue resistance in poly(methyl methacrylate) bone cement (PMMA) by centrifugation and titanium fiber addition were studied. Three modified bone cements were tested: porosity reduced cement (C-PMMA); titanium (Ti) fiber-reinforced cement (R-PMMA), using a novel method to incorporate fibers; and porosity reduced and Ti fiber-reinforced cement (C-R-PMMA). Specimens of untreated bone cement (PMMA) were included as controls. Non-notched and notched specimens were cyclically loaded in fully reversed bending. For the non-notched specimens, at all stress levels, C-R-PMMA had significantly greater fatigue life than either C-PMMA or R-PMMA (except C-PMMA at 30 MPa). R-PMMA had lower fatigue life than the control at 30 MPa (nominal maximum stress), but higher fatigue life at 20 and 15 MPa. At both 20 and 15 MPa, there was no statistical difference between the fatigue lives of C-PMMA and R-PMMA. Fractography revealed that, at 30 MPa, characteristics of rapid fracture predominated. At 20 and 15 MPa, in contrast, almost the entire fracture surface showed the characteristic fatigue morphology, indicating that subcritical crack growth was predominant. For the notched specimens, C-PMMA showed greater life than PMMA at the highest stress intensity, but the lifetimes converged with decreasing stress intensity. In contrast, the life-times for PMMA and R-PMMA diverged with decreasing stress intensity. The effect of centrifugation appeared to be strongest at higher stress intensities, and diminished with decreasing stress intensity. The reinforcing effect of Ti fiber addition increased the notched fatigue life at high initial stress intensities, and the reinforcing effect increased with decreased stress intensity.(ABSTRACT TRUNCATED AT 250 WORDS)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.