Abstract
The property of surface electron in undoped IIn0.13Al0.87N epilayers with different thicknesses has been investigated using x-ray photoemission spectroscopy (XPS) and micro-Raman scattering spectra. XPS has been used to determine the characteristic of the native oxide at the free surfaces of In0.13Al0.87N film. It is showed that the binding energy shift to higher with the thickness reduction from the Al 2p, N 1s, In 3d5/2 spectra. While, there is more native oxide at the surface of In0.13Al0.87N film with the decrease of thickness. In addition, a broad peak in high energy region was only observed in the thinnest In0.13Al0.87N epilayer from micro-Raman results, and it may be relative to L+ coupled mode of In0.13Al0.87N.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.