Abstract
AbstractThis study investigates the effect of tempering temperature on the microstructure and wear resistance of high-alloy white cast iron (Ni-Hard 4) with 1.15% W and 0.5% B additions. Specimens were austenitized at 850 °C for 5 h, quenched in air, and tempered at temperatures between 250 and 650 °C for 4 h. Equilibrium and non-equilibrium thermodynamic calculations were performed using Thermo-Calc software. After the microstructural investigations, hardness testing was carried out. A pin-on-disk tribometer was used to conduct wear tests under dry sliding conditions. Microstructure and worn surfaces were examined using light and scanning electron microscopes. The results showed that increasing tempering temperature resulted in a higher volume fraction of carbides. It was found that tempering at 550 °C for four hours increases resistance to wear giving the lowest measured values of weight loss and wear rate. Accordingly, tempering allows the precipitation of fine carbides in the martensitic matrix which may increase wear resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.