The effect of surface treatment and low-temperature degradation on flexural strength of additive manufactured zirconia

Abstract

This study aimed to assess the effect of low-temperature degradation (LTD) and surface treatment on the flexural strength of additive-manufactured (AM) zirconia by comparison to subtractive-manufactured (SM) zirconia. Disc-shaped zirconia specimens were fabricated using AM and SM technology, and each group was assigned to 3 subgroups according to the type of surface treatment: control, sandblasting (SB), and 9% hydrofluoric acid etching (HF). The groups were then further divided into 2 subgroups: unaged and aged. Biaxial flexural strength, crystal phase, surface topography, and surface roughness were measured to evaluate the mechanical properties. Statistical analyses were performed with 3-way ANOVA, followed by the comparison of means with Bonferroni post hoc analyses. The means and standard deviations of the biaxial flexural strength and Weibull parameters were calculated with descriptive statistics. All SM groups showed significantly greater flexural strength than the AM groups (p < .05), and LTD did not affect flexural strength except for the SMHF group (p < .05). After LTD, monoclinic phases (m-phase) were found in all groups, and SEM images showed grain pullout due to zirconia volume expansion in both control groups. Sandblasting significantly affected flexural strength (p < .05), whereas the HF group did not affect flexural strength except in the SMHF group after LTD (p < .05). No significant difference was observed in the surface roughness of AM compared to SM groups conditioned with the same surface treatment regardless of LTD. AM zirconia has comparable mechanical properties to SM zirconia, regardless of low-temperature degradation and surface treatment, which indicates the potential of the AM technique for clinical applications.