Abstract
Carbon fibre is not widely recycled due to the inconsistent tensile properties of the recycled carbon fibre (rCF). It is unclear whether the surface treatments for virgin carbon fibre (vCF) have an impact on the quality of rCF. This paper presents an experimental investigation into the effect of epoxy sizing and electrochemical oxidation for vCF on the tensile and surface properties of rCF recycled by pyrolysis. Carbon fibre with sizing, or surface oxidation, or both, experience a reduction in tensile strength by 44.6%, 43.7% and 50.1%, respectively, during the recycling process, compared to 19.8% for un-treated fibre. Surface-treated carbon fibres exhibit more surface defects (ID/IG from 1.6 to 2.7 from Raman spectroscopy) and a smaller average crystallite size (from 7.6 nm to 6.2 nm from X-ray diffraction) after recycling. The results indicate that the interactions between the sizing agent and surface functional groups contribute to the down-cycling of carbon fibre.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Composites Part A: Applied Science and Manufacturing
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.