The Effect of Sintering Temperature on The Rolled Silver-Sheathed Monofilament Bi,Pb-Sr-Ca-Cu-O Superconducting Wire

Abstract

The manufacture of high critical temperature (Tc) Bi, Pb-Sr-Ca-Cu-O (HTS BPSCCO) superconductor wire fabricated by power-in-tube (PIT) is a multi-step process. The main difficulty is that the value of Tc superconductor wire determined by various factors for each step. The objective of this research is to investigate the effect of sintering parameters on the properties of final rolled material. The fabrication process of 1 m rolled-silver sheath monofilament superconductor BPSCCO wire using mechanical deformation process including rolling and drawing has been carried out. The pure silver powders were melted and formed into pure silver (Ag) tube. The tube was 10 mm in diameter with a sheath material: superconductor powders ratio of about 6 : 1. Starting powders, containing the nominal composition of Bi2-Sr2-Cam-1-Cum-Oy, were inserted into the pure silver tube and rolled until it reached a diameter of 4 mm. A typical area reduction ratio of about 5% per step has been proposed to prevent microcracking during the cold-drawing process. The process of rolling of the silver tube was subsequently repeated to obtain three samples and then followed by heat-treated at 820 °C, 840 °C, and 860 °C, respectively. The surface morphology was analyzed by using SEM; the crystal structure was studied by using X-RD, whereas the superconductivity was investigated by using temperature dependence resistivity measurement by using four-point probe technique. SEM images showed the porosity of the cross-sectional surface of the samples. The sample with low heating temperature showed porosity more than the one with high temperature. The value of critical temperature (Tc) of the sample with a dwelling time of heating of 8 hours is 70 K. At above 70 K, it shows the behavior of conductor properties. However, the porosity increased as the heating time increased up to 24 hours. The critical temperature was difficult to be identified due to its porosity. According to XRD results, the Bi-2212 phase is prominent in all samples.