Abstract
In the present study, the effect of oxidation on the structure and the hardness of ternary (Zr, Hf)N coatings, whose Hf content was varied between 0 and 21 wt.%, has been systematically examined. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400oC for times up to 12 h in air. Ternary (Zr, Hf)N coatings are found to be more susceptible towards oxidation compared to binary ZrN coating. Oxidation caused the formation of a mixed oxide layer composed of ZrO2 and HfO2. Formation of oxide layer was accompanied by a reduction in hardness. Hardness values of Hf free and Hf alloyed (Zr, Hf)N coatings were very close to each other both in as-deposited and oxidized states.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.