Abstract
The experimental study herein presented was conducted aiming to evaluate the influence of nanosilica (nS) addition on properties of ultra-high performance concrete (UHPC). Thermo gravimetric analysis results indicated that nS consumes much more Ca(OH)2 as compared to silica fume, specifically at the early ages. Mercury intrusion porosimetry measurements proved that the addition of nS particles leads to reduction of capillary pores. Scanning electron microscope observation revealed that the inclusion of nS can also efficiently improve the interfacial transition zone between the aggregates and the binding paste. The addition of nS also resulted in an enhancement in compressive strength as well as in transport properties of UHPC. The optimum amount of cement replacement by nS in cement paste to achieve the best performance was 3 wt.%. However, the improper dispersion of nS was found as a deterrent factor to introduce higher percentage of nS into the cement paste.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.