The effect of high-irradiance rapid polymerization on degree of conversion, monomer elution, polymerization shrinkage and porosity of bulk-fill resin composites.

Abstract

The purpose was to compare the degree of conversion (DC), monomer elution (ME), polymerization shrinkage (PS) and porosity of two addition-fragmentation chain transfer (AFCT) modified resin-based composites (RBC) light-cured with rapid- (RP), turbo- (TP) or conventional polymerization (CP) settings. Cylindrical samples (6-mm wide, 4-mm thick) were prepared from Tetric PowerFill (TPF) and Filtek One Bulk (FOB). Four groups were established according to the polymerization settings: 3s-RP, 5s-TP, 10s-CP and 20s-CP. Samples in 1mm thickness with 20s-CP settings served as controls. The DC at the top and bottom surfaces was measured with micro-Raman spectroscopy. ME was detected with high-performance liquid chromatography. PS and porosity were analyzed by micro-computed tomography. ANOVA and Tukey's post-hoc test, multivariate analysis and partial eta-squared statistics were used to analyze the data (p<0.05). FOB showed higher DC values (61.5-77.5 %) at the top compared to TPF (43.5-67.8 %). At the bottom TPF samples achieved higher DCs (39.9-58.5 %) than FOB (18.21-66.18 %). Extending the curing time increased DC (except the top of FOB) and decreased ME. BisGMA release was the highest among the detected monomers from both RBCs. The amount was three-fold more from TPF. The factor Material and Exposure significantly influenced DC and ME. PS (1.8-2.5 %) did not differ among the groups and RBCs except for the lowest value of TPF cured with the 3s_RP setting (p=0.03). FOB showed 4.5-fold lower porosity (p<0.001). Significantly higher pore volume was detected after polymerization in 3s_RP (p<0.001). High-irradiance rapid 3-s curing of AFCT modified RBCs resulted in inferior results for some important material properties. A longer exposure time is recommended in a clinical situation.