Abstract
Study wear resistance for heat treatment of Ni-B-CNT electroless coatings. Different concentrations for CNT (0 ,0.35 and 0.7 g/l Ni-B-CNT composite coatings deposition on 4340 steel. After the procedure of coating, all samples were heat treatment. The test wear of a coating was valued with pin on disk technique. Preparation of Ni–B–CNT electroless coatings are with using nickel chloride in alkaline bath, borohydride and Multi walled carbon nanotubes. characterization with FESEM, micro hardness, XRD and surface roughness. Study for surfaces of worn with EDS and FESEM. Micro hardness results are show that the larger hardness1010 HV is gained by heat treatment for coating (Ni-B- 0.35 g/L CNT) because of concentration CNT caused structure conversion for coating Ni-B from amorphous to crystalline. Also, CNT prevent maximum heat production and decrease of the friction coefficient during test wear. CNT aggregation was noted result the presence for more particles (Ni-B - 0.7g/l CNT) that occur create roughness and also lead to increase in rate of wear because of big particles with weakly joined in matrix of Ni.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.