Abstract
Abstract Nanocrystalline nickel produced by pulsed electrolysis was heat-treated to produce grain sizes from nanoscale to microscale. A special polish allowed to image the specimen with an atomic force microscope (AFM) down to a grain size of 30 nm. Micro- and instrumented nanohardness of these specimens were examined. A NI-AFM (Nanoindenting AFM) was used to measure the interaction between grain boundaries and dislocations. Nanoindentation was performed always in the center of the grains. When the size of the indent was kept constant (constant strain) it could be shown that the hardness scales with the dislocation density within the grains. However, when the size of the indent approached the grain size, the plastic zone spread over several grains and a decrease in hardness was observed. In addition, with deceasing grain size, grain boundary sliding was observed even at room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.