Abstract
A series of annealing parameters including the cooling rate and overaging time, especially ultra high cooling rate of a ultra-low carbon auto steel were conducted on HDPS (hot dipping process simulator) in experiment. The research results show that, when samples were conducted under extra fast cooling rate higher than 30 °C/s, yield and tensile strength almost changed not when cooling rate increased from 30 to 50 °C/s, as cooling rate reached 90 °C/s, the strength and elongation changed more rapidly. When the overaging time changed from 130 to 300 s, the elongation was more sensitive, changed from 19.7 to 25.6 %. Yield and tensile strength were not sensitive when aging time was below 213 s, but with increasing aging as high as 300 s, the yield strength decreased 11 MPa, and tensile strength decreased 21 MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.