Abstract
Effect of methyl methacrylate (MMA) as a binder and heating treatment were investigated to improve green alumina compacts machinability. Properties of green compacts and their corresponding sintered samples prepared with and without MMA were compared. Investigation of green and sintered properties was performed on samples compacted at applied pressures up to 150 MPa. After pressing, samples with MMA were thermally treated at 115oC. The intention was to enhance the polymerization of MMA at a temperature a little higher than the glass transition temperature (Tg = 103oC) of poly (methyl methacrylate). Green compacts with MMA had higher green density values than those without MMA. Sintered samples with MMA had lower values of sintered density and higher values of total porosity; after sintering, relative linear shrinkage was around 15 % for the whole range of applied pressures. The possibility of easily machining the green compacts with MMA produces great possibilities for application in many fields
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.