Abstract
The purpose of this study was to investigate the effect of two solutions differing by pH (6.4 and 4.0) and the use of a setting accelerator (15% Na 2HPO 4 solution) on the properties of white-colored mineral trioxide aggregate (WMTA). These studies indicated that pH 4.0 had a deleterious effect on the morphology of WMTA mixed with water, however, not for WMTA mixed with Na 2HPO 4. When immersed in a pH 4.0 solution for 7 days, WMTA mixed with water or Na 2HPO 4 achieved a diametral tensile strength of 7.9 and 9.0 MPa, respectively, which was significantly lower (p < 0.05) than those obtained at pH 6.4 (11.2 and 12.0 MPa) but significantly higher (p < 0.05) than day 0 samples (4.4 and 4.8 MPa). Mixing WMTA with the accelerator did not significantly affect the microstructure, solubility, or strength in an acidic environment.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.