Abstract
The purpose of this study was to investigate the effect of a sodium phosphate dibasic (Na2HPO4) setting accelerator on the properties of white-colored mineral trioxide aggregate (WMTA). Setting times were measured by using a Gilmore needle. Changes in the pH value, diametral tensile strength, and phase composition of WMTA were evaluated. By using a 15% Na2HPO4 solution as a liquid phase mixed with WMTA, the setting time was significantly reduced to 26 minutes rather than the usual 3 hours. The 15% Na2HPO4 promoted WMTA to achieve a maximum diametral tensile strength of 4.9 MPa at an initial 6-hour aging time and 1 MPa for the cement mixed with water. The pH value of the 15% Na2HPO4-mixed cement was changed from an initial 11.0 to a high of 13.2, which was similar to the results using water. The results suggest that the Na2HPO4 solution may be an effective setting accelerator for WMTA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.