Abstract
The effects of thickness and delamination on the fracture toughness and stable crack growth behaviour of high-toughness pipeline steels were investigated experimentally by use of compact tension specimens with thicknesses of 3–15 mm cut from a 17 mm-thick wall pipe. Material resistance curves were generated based on the stress intensity factor (SIF) K and the J-integral. The critical SIF K c and the J-resistance curves are found to be independent of thickness as the delaminations near the crack tip within the material reduce the out-of-plane constraint in thicker specimens. Both fracture mechanism and mechanics analyses shown that the fracture behaviour of the steel is controlled by the strong-coupled effects of thickness and delaminations. With increasing thickness, the out-of-plane stress constraint increases and causes the inclusion separation, growth and coalescence to form delaminations of different sizes before the main crack initiates. The delaminations in turn, reduce the out-of-plane constraint and thus, the thickness effect upon fracture. The advantages and disadvantages of delaminations in a safety assessment of pipelines are also discussed based on three-dimensional fracture theory.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.