Abstract
First two to five barriers in the growth sequence having silicon (Si) doping of eight periods In0.2Ga0.8N/GaN quantum wells (QWs) on twenty pairs of In0.02Ga0.98N/GaN superlattice strain relief layers (SRLs) of blue LEDs were prepared by low pressure metal–organic chemical vapor deposition (LPMOCVD) system on patterned sapphire substrates (PSSs). The effect of doping layers on the luminescence properties of QWs of blue LEDs was investigated. For the sample with first four barriers having Si doping, formation of soft confinement of QWs potential and strong carrier localization inside QWs were occurred. There is better spread of carriers among eight QWs and strong radiative recombination of carriers inside QWs. The increase of output power and external quantum efficiency (EQE) is due to decrease of Auger processes, leakage of carriers out of QWs, and nonradiative recombination centers. The consequences demonstrate that first four barriers with Si doping possess the favorable doping condition for eight periods In0.2Ga0.8N/GaN QWs.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.