Abstract
This paper investigates the effects of electrically induced and direct tensile stress on the deformation and dielectric properties of Pb(Zn1/3Nb2/3)O3-(6-7)%PbTiO3 single crystals of [110]L× [001]T cut by using a unimorph sample and a four-point-bend (FPB) sample, respectively. The results show a dip in tip displacement for the unimorph sample at sufficiently high electric field parallel to the poling field direction and a sudden rise in capacitance for the FPB sample at sufficiently high tensile stress in the [110] crystal direction, respectively. These phenomena are attributed to the tensile stress induced rhombohedral-to-orthorhombic phase transition and associated depolarization events in the crystal. For the said crystal cut, the obtained tensile depoling stress is in the range of 15-20 MPa. The present work furthermore shows that the occurrence of tensile stress-induced depolarization is possible even when the direction of the applied electric field is parallel to the poling field direction, as in the unimorph sample examined.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.