Tensile properties of chrome tanned leather waste short fibre filled unsaturated polyester composite

Abstract

Waste leather from industries was commonly disposed via land filling or incineration where the oxidation of Cr III to Cr VI by oxidants (such as peroxides and hypohalide) can easily occur. Cr VI is well known as carcinogenic and mutagenic element where the excessive exposure to this element can be very harmful. As an alternative way, the leather waste from footwear industry was utilised as filler in unsaturated polyester composite (UPC). The leather waste was ground using 0.25 mm mesh size and used without any chemical treatment. The sample was fabricated via castingtechnique and the study was carried out at 1 wt%, 2 wt% and 3 wt% filler loading. The leather waste filled composites showed lower tensile strength and Young’s modulus than the unfilled composite. The increasing loading amount of leather waste led to the decreased in tensile strength and Young’s modulus. The tensile results was supported by the decreasing pattern of density result which indicates the increasing of void content as the filler loading increased. The results of glass transition temperature are also parallel to the tensile properties where the increasing filler loading had decreased the glass transition temperature. Based on the morphological observation on the fractured tensile sample, much severe filler agglomerations and higher amount of voids was observed at higher filler loading compared to the lower filler loading.