Abstract
The effects of fast neutron irradiation on tensile and transient burst properties of advanced ferritic/martensitic steel claddings for fast breeder reactors were investigated. Specimens were irradiated in the experimental fast reactor JOYO using the material irradiation rig at temperatures between 773 and 1013 K to fast neutron doses ranging from 11 to 102 dpa. The post-irradiation tensile and temperature-transient-to-burst tests were carried out. The results of mechanical tests showed that there was no significant degradation in tensile and transient burst strengths after neutron irradiation below 873 K. This was attributed to grain boundary strengthening caused by precipitates that preferentially formed on prior-austenite grain boundaries. Both strengths at neutron irradiation above about 903 K up to 102 dpa decreased due to radiation enhanced recovery of lath martensite structures and recrystallization.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.