Temperature and electric field induced metal-insulator transition in atomic layer deposited VO2 thin films

Abstract

Amorphous vanadium oxide (VO2) films deposited by atomic layer deposition (ALD) were crystallized with an ex situ anneal at 660–670°C for 1–2h under a low oxygen pressure (10−4 to 10−5Torr). Under these conditions the crystalline VO2 phase was maintained, while formation of the V2O5 phase was suppressed. Electrical transition from the insulator to the metallic phase was observed in the 37–60°C range, with an ROFF/RON ratio of up to about 750 and ΔTC≅7–10°C. Lateral electric field applied across two-terminal device structures induced a reversible phase change, with a room temperature transition field of about 25kV/cm in the VO2 sample processed with the 2h long O2 anneal. Both the width and slope of the field induced MIT I-V hysteresis were dependent upon the VO2 crystalline quality.