Abstract
The magnetostriction of the Fe82Ga15Al3 alloy, along the length and width, can be tailored by applying a magnetic field heat treatment. In this work, the Fe82Ga15Al3 sheet was cut from the directional solidified Fe82Ga15Al3 alloy with the ⟨100⟩ preferred orientation and was annealed at 720 °C for 30 min under a magnetic field of 800 Oe along the length direction with a heating and cooling rate of 100 °C/min. The magnetostrictive properties along the length and width directions were modified to λ// = 7 ppm and λ⊥ = −210 ppm from λ// = 210 ppm and λ⊥ = −10 ppm for the initial sample prior to the magnetic field heat treatment. The cellular-like magnetic domain structure was composed of parallel 180° stripe domains and vertical 90° domains observed using a magnetic-force microscope. The change in magnetostriction along parallel and perpendicular directions was mainly resulted from the rotation of the magnetic domain units.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.