Abstract
PurposeThis paper aims to optimize the erosion wear analysis of slurry impeller material. Stainless steel (SS-410) was used as the pump impeller material. This erosion test was established to influence the rotational speed, solid concentration, time period and particle size. Fly ash was used as the erodent material.Design/methodology/approachThe erosion wear experiments were performed at different particle size, rotational speed, time duration and solid concentration (by weight). These tests were performed at four different speeds of 750, 1,000, 1,250 and 1,500 rpm, and the time durations of these experiments are 75, 120,165 and 210 min. For protective coating, high-velocity oxygen-fuel spray process was used for depositing WC-10Co-4Cr coating on stainless steel. To investigate the influence of controlled process parameters on slurry erosion wear of pump impeller material, Taguchi method was used.FindingsResults show that significant improvement in erosion wear resistance has been observed by using WC-10Co-4Cr coating. The process parameters affecting the erosion wear loss were in following order: time > rpm > concentration > particle size. The means of signal-to-noise ratio of stainless steel SS410 with and without coating vary from 93.56 to 54.02 and from 86.02 to 48.18, respectively.Originality/valueFor the erosion wear rate of both uncoated and coated stainless steel, the most powerful influencing factor was identified as time. The erosion test reveals that the coating exhibits ductile erosion mechanism and shows better erosion wear resistance (approximately two times) compared to uncoated stainless steel.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.