Abstract
Rutile titania nanocrystalline particles with high specific surface areas were directly prepared by thermal hydrolysis of titanium tetrachloride aqueous solution. The as‐prepared rutile titania powder was characterized by X‐ray diffraction (XRD), transmission electron microscopy (TEM), Brunauer–Emmett–Teller surface area analysis, and Fourier transform Raman and IR spectroscopies. Neither anatase nor amorphous titania could be detected in this titania powder by XRD, Raman spectroscopy, and high‐resolution TEM. In the phenol degradation reaction, the rutile titania powder with an initial crystalline size of 7 nm was found to have higher photocatalytic activity than that of anatase titania with the same specific surface area. The rutile titania powders calcined at 300° and 450°C also showed a relatively high photocatalytic property. The high activity of the as‐prepared rutile titania was attributed to the abundance of hydroxy groups in the powder, as was proven by thermogravimetric analysis data, which provided more active sites for the degradation reaction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.