Abstract
AbstractIn this paper, macroporous high‐entropy spinel oxide (HESO) (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 monoliths were successfully fabricated via a sol–gel method followed by calcination. Appropriate polyacrylic acid and propylene oxide contents allow the formation of three‐dimensional co‐continuous xerogel monoliths, and the water/glycerol ratio controls the macropore size of monoliths. Subsequent calcination achieves the precipitation of HESO (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 with a singular phase and exceptional structural stability. The macroporous HESO (Fe0.2Ni0.2Co0.2Mn0.2Zn0.2)3O4 demonstrates remarkable performance in the oxygen evolution reaction (OER) with an overpotential of 333 mV at 100 mA cm−2 and a Tafel slope of 43.2 mV dec–1, surpassing that of RuO2 (391 mV) under identical conditions. Furthermore, the catalytic stability of the HESO catalyst remains superior even after 24 h of testing. This process offers a promising avenue for the development of macroporous high‐entropy oxide OER catalysts for overall water splitting.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.