Abstract
This study presents the synthesis of (TiZrHfTaNb)C, (TiTaNb)0.45Hf0.275Zr0.275С and (TiTaNb)0.3Hf0.35Zr0.35С single-phase, high-entropy carbides through mechanical alloying and plasma sintering. High-entropy carbides hold promise for applications in jet engine components. We identified optimal mechanical alloying conditions to achieve powder homogeneity and minimize iron fouling. The microstructure, phase, and chemical compositions of the samples were investigated. At 1600 °C, a sample with a face-centered cubic (FCC) lattice and low content of zirconium and hafnium oxides was formed. Elevating the sintering temperature to 2000 °C facilitated oxide dissolution and the formation of single-phase, high-entropy carbides. The microhardness of the samples ranged from 1600 to 2000 HV, while the compressive strength varied between 600 and 800 MPa. Plasma heating tests demonstrated excellent resistance to thermal oxidation for (TiTaNb)0.3Hf0.35Zr0.35С, withstanding temperatures up to 2250 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.