Synthesis of targeted doxorubicin-loaded gold nanorod −mesoporous manganese dioxide core–shell nanostructure for ferroptosis, chemo-photothermal therapy in vitro and in vivo

Abstract

In the current study, a core–shell inorganic nanostructure comprising a gold nanorod core and −mesoporous manganese dioxide shell was synthesized. Then, the mesoporous manganese dioxide shell was loaded with doxorubicin (DOX) and then coated with pluronic F127 and pluronic F127-folic acid conjugate (1.5:1 wt ratio of pluronic F127: pluronic F127-folic acid conjugate) to prepare targeted final platform. In this design, mesoporous manganese dioxide acted as a reservoir for DOX loading, anti-hypoxia, and MRI contrast agent, while the gold nanorod core acted as a photothermal and CT scan imaging agent. DOX was encapsulated in the mesoporous manganese dioxide shell with a loading capacity and loading efficiency of 19.8 % ± 0.2 and 99.0 % ± 0.9, respectively. The in vitro release experiment showed the impact of glutathione (GSH), mildly acidic pH, and laser irradiating toward accelerated stimuli-responsive DOX release. The ·OH production of the prepared platform was verified by methylene blue (MB) decomposition reaction. Furthermore, thermal imaging exhibited the ability of the prepared platform to convert the NIR irradiation to heat. In vitro cytotoxicity tests on the folate receptor-positive 4 T1 cell line revealed the remarkable cytotoxicity of the targeted formulation compared to the nontargeted formulation (statistically significant). The MTT experiment demonstrated that exposure to laser 808 irradiation enhanced cytotoxicity of the targeted formulation (p < 0.0001). The production of ROS in 4 T1 cells following treatment with the targeted formulation was demonstrated by the dichloro-dihydro-fluorescein diacetate (DCFH-DA) assay. Furthermore, in vivo investigations by implementing subcutaneous 4 T1 tumorized female BABL/c mice indicated that the prepared platform was an effective system in suppressing tumor growth by combining chemotherapy with PTT (photothermal therapy). Additionally, simultanous PTT and anti-hypoxic activity of this system showed potent tumor growth suppression impact. The percent of tumor size reduction in mice treated with FA-F127-DOX@Au-MnO2 + 808 nm laser compared to the control group was 99.7 %. The results of the biodistribution investigation showed tumor accumulation and modified pharmacokinetics of the targeted system. Lastly, 6 and 24 h post-intravenous injection, CT-scan and MR imagings capability of the prepared platform was verified in preclinical stage. The prepared multipurpose system introduces great opportunity to provide multiple treatment strategy along with multimodal imaging capability in a single platform for breast cancer treatment.