Abstract
The composition of Hydroxyapatite (HAp) is expressed by the formula Ca10(PO4)6(OH)2. Many reports have been published on the synthesis of HAp in which Ca ions are substituted by various cations (e.g., Sr, Ba). On the other hand, studies on the synthesis of sulfate-ion-substituted hydroxyapatite (SAp) have rarely been conducted. The present study investigated the conditions for the synthesis of SAp from amorphous calcium phosphate (ACP, Ca3(PO4)2• nH2O) as the starting material, which can readily incorporate various ions into its structure. Sodium sulfate (Na2SO4) was added to ACP, and then, the mixture was hydrothermally processed at 220°C for 3 h. SAp obtained under these conditions had a Ca-deficient-type HAp structure. The SO4/PO4 molar ratio in SAp increased with increasing amounts of added Na2SO4, reaching a maximum value of 0.5, meaning that 1/3 of the PO4 3– ions contained in HAp were substituted by SO4 2– ions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.