Synthesis of solid sodium silicate from waste glass and utilization on one-part alkali-activated materials based on spent oil filtering earth.

Abstract

Alkali activated materials (AAMs) commonly known as geopolymers are considered ecofriendly substitutes for Portland cement. However, these materials still have a significant environmental impact, owing mainly to the use of activators based on commercial chemical products. In this sense, this research focuses on the production and use of waste glass-derived activators AAMs as an alternative to commercial activators. Using a thermochemical synthesis method, activator compositions were systematically designed to achieve predefined activator modulus (Ms = SiO2/Na2O = 0.5; 1.0 and 1.5). These alternative activators were studied by XRD, FTIR and SEM techniques. Additionally, one-part AAMs were manufactured using spent oil filtration earth (SOFE) as precursor and activator with optimum modulus Ms = 1.0. The influence of the Na2O dosage was studied (10; 20 and 30g of Na2O per every 100g of SOFE) as well as the influence of the activator modulus maintaining the optimum dosage of 20g Na2O per 100g of SOFE. As a control, two-part AAMs were also synthetized with the optimum dosage and modulus employing commercial activators (NaOH + Na2SiO3 solution). Results indicate that the modulus of the alternative activator and especially the Na2O dosage have a significant influence on the technological properties of AAMs based in SOFE, with an optimum compressive strength (35.8MPa) for the addition of 20g of Na2O per every 100g of SOFE using activator with modulus Ms = 1.0. This research embodies a sustainable approach to AAM production and suggests waste glass as a valuable raw material for sodium silicate synthesis intended for the one-part activation of spent filtering earth from the agri-food industry, aligning with the principles of circular economy and sustainable development goals.