Abstract
Abstract A study was undertaken to production of Si 3 N 4 powders by carbo-thermal reduction and nitridation (CTRN) of diatomite. Test samples were prepared by mixing 99% purity and mean powder size of 2.4 μm of carbon black and maximum particle size of 150 μm diatomite with C/SiO 2 molar ratio 4. Prepared sample was subjected to CTRN process at temperatures of 1300, 1350, 1400, and 1450 °C for 4, 8, and 16 h. CTRN process was conducted in an atmosphere controlled tube furnace in nitrogen flow 5 cm 3 /min. All products were examined by XRD and SEM-EDX to determine the transformation, morphology and chemical composition. The results showed that the best Si 3 N 4 transformation occurred at 1400 °C for 16 h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.