Synthesis of Microporous Materials and Their VSC Adsorption Properties

Abstract

Oral malodor is caused by volatile sulfur compounds (VSC) such as hydrogen sulfide (H2S), methyl mercaptan and dimethyl sulfide produced in mouth. VSC induces permeability of mucous membrane and oral malodor formation. Thus, the adsorbent which highly adsorbs VSC should be useful for health in mouth and may prevent teeth from decaying. The microporous material, hydrotalcite, was synthesized by a wet method, and the H2S adsorption was studied. The samples, identified by powder X-ray diffraction method, were put into glass flask filled with H2S gas. The initial concentration of H2S was 30 ppm. The change in concentrations of H2S was measured at rt, and the amount of H2S absorbed on the hydrotalcite for 24 h was 300 micro L/g. The samples were taken out from the above glass flask and put into a pyrolysis plant attached to gas chromatography-mass spectrometry to determine the amount of H2S desorbed from samples. Only 3 % of H2S was desorbed when heated at 500 °C. H2S in water was also found to adsorb into hydrotalcite, which was confirmed by the headspace gas chromatography with flame photometric detector. The hydrotalcite material should be expected to be an adsorbent material, useful for health in mouth.